Iron-based Alloy Powder Material

description 
powder material of iron-based alloy is composed of stainless steel 304, 316L and stamping steel 1.2709. This material is used in the automotive, meditsinstkoy industry, manufacturing industry, the manufacture of filters, pumps, structural components of cars and others. This iron powder differs corrosion resistance and low cost.

1. The powder material stainless stli 304 Unit:%

Al	Co	Cr	Cu	Mn	Ni	Si	O	content of impurities	Fe
0.1	0.2	19.1	0.3	1.15	8.96	1.37	0.051	≤0.3	Bal

particle size (μm)	0 - 15	15 - 45	15 -53	45 - 105	105 - 150
Flow (sec / 50g)	≤15
density (g / cm3)	4.12	4.30	4.32	4.51	4.54

2. The powder material stainless stli 316L (0Cr17Ni12Mo2) Unit:%

Ni	Cr	Mo	Si	Mn	P	S	C	O	Fe
10 - 14	16 - 18	2 - 3	≤1	≤2	≤0.045	≤0.03	≤0.08	0.025 - 0.055	Bal

particle size (μ)	0 - 15	15 - 45	15 - 53	45 - 105	105 - 150
Flow (sec / 50g)	≤15
density ((g / cm3)	4.4	4.62	4.65	4.77	4.81

3. Proshkovy material from alloy SALT stamping steel 1.2709 (X3NiCoMoTi18-9-5) Unit:%

Ni	Co	Mo	Ti	Al	Cr		Cu	C	Mn	Si	P	S		O	Fe
					≤				≤		≤
17 - 19	8.5 - 9.5	4.5 - 5.2	0.6 - 0.8	0.05 - 0.15	0.5	0.5		0.03	0.1	0.1	0.01		0.01	0.05	Bal

chaastits size (μ)	0 - 15	15 - 45	15 - 53	45 - 105	105 -150
Flow (sec / 50g)	≤15
density (g / cm3)	4.52	4.68	4.70	4.87	4.93